Comparison Chart of
Fluoroplastic Resins
|
The
table below lists a generally accepted summary of properties that we
believe to be reliable. Please note that many of these resins
are produced in several varieties and property characteristics may
vary. Therefore, determination of resin is dependent on the
application and this table is only meant to serve as a general
guideline. There are 2 tables on this page.
Go Back
|
|
PTFE,
FEP, PFA, ETFE, ECTFE |
PVDF,
MFA, THV, PEEK, ULTEM |
(If you would like to view the properties of a particular
resin, click on the hyperlink in the chart below)
Property
Comparison of Fluoroplastic/Fluoropolymer Resins |
Properties |
ASTM
or Unit |
PTFE |
FEP |
PFA |
ETFE |
ECTFE |
MECHANICAL
PROPERTIES |
Specific
Gravity |
D792 |
2.18 |
2.15 |
2.15 |
1.74 |
1.68 |
Elongation
% |
D638 |
200~400 |
250~330 |
280~300 |
420~450 |
200~300 |
Tensile
Strength (psi) |
D638 |
2,000~5,000
|
2,700~3,100 |
4,000~4,500 |
6,100~6,800
|
6,000~7,000
|
Flexural
Strength (psi) |
|
no break |
no break |
no break |
no break |
6,800 |
Compressive
Strength |
D695 |
710~860 |
710~860 |
710~860 |
1,550 |
1,276~1,711 |
Tensile
Elastic Modulas
(Young's Modulas) (psi) |
D638 |
57,000 |
50,000 |
N/A |
85,000~
95,000 |
240,000 |
(psi)
Flexural
Modulas
103MPa
(103kgf/cm2) |
D790 |
71,000~
85,000 |
78,000~
92,000 |
94,000~
99,000 |
128,000~
171,000 |
240,000 |
D790 |
0.5-0.6
(5.0-6.0) |
0.5-0.6
(5.5-6.5) |
0.6-0.7
(6.6-7.0) |
0.9-1.4
(9.0-14.0) |
1.4-1.8
(14-18) |
Flex
Life
(MIT cycles) |
D2176 |
>1,000,000 |
5,000~
80,000 |
10,000~
500,000 |
10,000~
27,000 |
n.a |
Hardness
Durometer Shore D |
D636 |
50~65 |
55 |
60 |
75 |
75 |
Coefficient
of Friction Static |
D1984 |
0.02 |
0.05 |
0.04~0.05 |
0.06 |
0.08 |
Abrasion
Resistance
1000 revs. |
Taber |
12 |
14.8 |
n.a |
n.a |
0.005 |
Impact
Strength IZOD
73°F/23°C, notched
ft/lbs/in |
D256 |
3.0 |
no breakdown |
no breakdown |
no breakdown |
2.5~2.7 |
THERMAL
PROPERTIES |
Melting
Point |
°C
(°F) |
327
(621) |
260
(500) |
305
(582) |
267
(512) |
240
(464) |
Upper
Service
Temperature(20,000h) |
°C
(°F) |
260
(500) |
204
(400) |
260
(500) |
150
(302) |
150-170
(300-340) |
Flame
Rating** |
UL
94 |
VO |
VO |
VO |
VO |
VO |
BTU/hr/sq
ft/deg F in
Thermal
Conductivity
cal/sec/cm2,ºC/cm |
|
1.7 |
1.4 |
1.32 |
1.65 |
n.a |
C117 |
6
x 10-4 |
n.a |
6
x 10-4 |
5.7
x 10-4 |
4.7~5.3
x 10-4 |
Heat of
Fusion |
BTU/LB
cal/g |
29-37 |
11 |
13 |
20 |
n.a |
Heat
of Combustion |
BTU/LB
cal/g |
2200 |
2200
1840 |
2300 |
5900
3730 |
n.a |
Low
Temperature Embrittlement |
°C
(°F) |
-268
-450 |
-268
-450 |
-268
-450 |
-104
-155 |
-76
-105 |
ELECTRICAL
PROPERTIES |
Dielectric
Constant |
D150/103Hz |
2.1 |
2.1 |
2.1 |
2.6 |
2.5 |
D150/106Hz |
2.1 |
2.1 |
2.1 |
2.6 |
2.4 |
Dissipation
Factor |
D150/103Hz |
n.a |
n.a |
n.a |
n.a |
n.a |
D150/106Hz |
n.a |
n.a |
n.a |
n.a |
n.a |
Dielectric
Strength |
125
MIL V.
10 MIL V. |
500
>1400 |
500
>1400 |
500
>2000 |
n.a
>
2000 |
n.a
n.a |
Volume
Resistivity ohm-cm |
D257 |
>1018 |
>1018 |
>1018 |
>1016 |
>1016 |
Surface
Resistivity
ohm/sq. |
|
>1018 |
>1016 |
>1017 |
>1014 |
n.a |
GENERAL
PROPERTIES |
Chemical/Solvent
Resistance |
|
Excellent |
Excellent |
Excellent |
Excellent |
Excellent |
Water
Absorption, 24h |
% |
<0.01 |
<0.01 |
<0.03 |
<0.03 |
Less
than 0.1% |
Refractive
Index |
|
1.35 |
1.338 |
n.a |
n.a |
n.a |
%
Arc
Resistivity
sec |
|
>300 |
>300 |
>300 |
75 |
n.a |
D495 |
>200 |
>300 |
>300 |
122 |
135 |
Properties |
ASTM
or Unit |
PTFE |
FEP |
PFA |
ETFE |
ECTFE |
Property
Comparison of Fluoroplastic/Fluoropolymer Resins |
Properties |
ASTM
or Unit |
PVDF |
MFA |
THV |
PEEK |
ULTEM |
MECHANICAL
PROPERTIES |
Specific
Gravity |
D792 |
1.8 |
2.12~2.17 |
195~1.98 |
1.30 |
1.27~1.51 |
Elongation
% |
D638 |
435 |
300~600 |
600~500 |
20~50 |
60 |
Tensile
Strength (psi) |
D638 |
4500-6200
|
3400-4500 |
2900~4060 |
14100~14500
|
16,500
|
Flexural
Strength (psi) |
|
8600-9500 |
n.a |
n.a |
25,000 |
20,000 |
Compressive
Strength |
D695 |
5,800 |
n.a |
n.a |
17,110 |
22,000 |
Transversal
Contraction
(Poisson's Ratio) |
|
0.35 |
n.a |
n.a |
0.4 |
n.a |
Tensile
Elastic Modulas
(Young's Modulas) (psi) |
D638 |
160,000 |
n.a |
n.a |
522,000 |
475,000 |
(psi)
Flexural
Modulas
103MPa
(103kgf/cm2) |
D790 |
140,000 |
n.a |
12,000~30,000 |
594,000 |
500,000 |
D790 |
n.a |
n.a |
n.a |
38 |
n.a |
Flex
Life
(MIT cycles) |
D2176 |
n.a |
n.a |
n.a |
n.a |
n.a |
Hardness
Durometer Shore D |
D636 |
72 |
59 |
44~58 |
n.a |
n.a |
Coefficient
of Friction Static |
D1984 |
02~04 |
0.2 |
n.a |
.24 |
n.a |
Abrasion Resistance
1000 revs. |
Taber |
n.a |
n.a |
n.a |
n.a |
n.a |
Impact
Strength IZOD
73°F/23°C, notched
ft/lbs/in |
D256 |
20.7 |
no breakdown |
no breakdown |
1.16~1.84 |
no
breakdown |
THERMAL
PROPERTIES |
Melting
Point |
°C
(°F) |
178
(352) |
285
(545) |
120-165
(248-328) |
334
(633) |
n.a |
Upper
Service
Temperature(20,000h) |
°C
(°F) |
129
(625) |
260
(500) |
150
(302) |
315
(599) |
200
(392) |
Flame
Rating** |
UL
94 |
VO |
VO |
VO |
VO |
VO |
BTU/hr/sq
ft/deg F in
Thermal
Conductivity
cal/sec/cm2,ºC/cm |
|
n.a |
n.a |
n.a |
n.a |
n.a |
C117 |
3.0x10-4 |
n.a |
n.a |
n.a |
n.a |
Heat of
Fusion |
BTU/LB
cal/g |
n.a
4,390 |
n.a
n.a |
n.a
n.a |
n.a
n.a |
n.a
n.a |
Heat
of Combustion |
BTU/LB
cal/g |
n.a
n.a |
n.a
n.a |
n.a
n.a |
n.a
n.a |
n.a
n.a |
Low
Temperature Embrittlement |
°C
(°F) |
-62
(-80) |
-232
(-450) |
n.a
n.a |
-65
(-85) |
n.a
n.a |
ELECTRICAL
PROPERTIES |
Dielectric
Constant |
D150/103Hz |
n.a |
2 |
n.a |
n.a |
n.a |
D150/106Hz |
n.a |
2 |
n.a |
n.a |
n.a |
Dissipation
Factor |
D150/103Hz |
n.a |
n.a |
n.a |
n.a |
n.a |
D150/106Hz |
n.a |
n.a |
n.a |
n.a |
n.a |
Dielectric
Strength |
125
MIL V.
10 MIL V. |
1700
n.a |
n.a
n.a |
n.a
n.a |
480
n.a |
830
n.a |
Volume
Resistivity ohm-cm |
D257 |
1.5
x 1015 |
n.a |
n.a |
4.9
x 1016 |
6.7
x 1016 |
Surface
Resistivity
ohm/sq. |
|
n.a |
n.a |
n.a |
n.a |
n.a |
GENERAL
PROPERTIES |
Chemical/Solvent
Resistance |
|
Very
Good |
Excellent |
Excellent |
Very
Good |
Good |
Water
Absorption, 24h |
% |
.04 |
n.a |
n.a |
0.68 |
0.25 |
Refractive
Index |
|
1.42 |
n.a |
1.35 |
2.15 |
1.63-1.68 |
%
Arc
Resistivity
sec |
|
n.a |
n.a |
n.a |
n.a |
n.a |
D495 |
50~60 |
240 |
n.a |
n.a |
n.a |
Properties |
ASTM
or Unit |
PVDF |
MFA |
THV |
PEEK |
ULTEM |
|